H11 Tool Steel – Economizer

Pre-machined H11 tool steel with machining allowance. Both bar ends saw cut.

H11 (1.2343) is a 5% chromium hot work tool steel. Compare to H13, H11 has less vanadium giving it higher toughness, with some reduction in wear resistance and temper resistance. H11 has excellent dimensional stability during heat treatment.

Typical chemical composition of H11 Tool steel (1.2343)
C Mn P S Si Cr V Mo
0.25-0.45% 0.20-0.60% 0.03% 0.03% 0.80-1.25% 4.75-5.50% 0.30-0.60% 1.10-1.60%

Tolerances

Thickness: -0.00/+0.20 mm
Width: -0.00/+0.40 mm
Square: +0.40/+0.40 mm
Length: +5.00/+30.00 mm

  • Thickness and width of material in ground/fine milled execution
  • Both bar ends saw cut
  • Surface roughness max. 3.2 µm
  • Rust protected, wrapped in VCI-paper

H11 Economizer – Pre-machined – Sold in 500 mm or 1000 mm lengths

 Thickness:
4.2 5.2 6.2 8.2 10.4 12.4 15.4 16.4 20.4 22.4 25.4 30.4
 Width: 10.4 X X X X X
12.4 X X X X X X
15.4 X X X X X X X
16.4 X X X X X X X
20.4 X X X X X X X X X
25.4 X X X X X X X X X X
30.4 X X X X X X X X X X X X
32.4 X X X X X X X X X X X X
40.4 X X X X X X X X X X X X
50.4 X X X X X X X X X X X X
60.4 X X X X X X X X X X X X
63.4
70.4 X X X X X X X X X X X X
80.4 X X X X X X X X X X X X
90.4 X X X X X X X
100.4 X X X X X X X X X X X X
110.4 X X X
120.4 X X X X X X X
130.4 X X X X X
140.4 X X X X X X
150.4 X X X X X X X X X X
160.4 X X X X X X X X
180.4 X X X X
200.4 X X X X X X X X X X
250.4 X X X X X X X X X
300.4 X X X X X X X X
350.4 X X X
405 X X X X X X X
505 X X X X X X X X X
Width 32.4 40.4 50.4 60.4 63.4 70.4 80.4 90.4 100.4 120.4 150.4
10.4
12.4
15.4
16.4
20.4
25.4
30.4
32.4 X
40.4 X X
50.4 X X X
60.4 X X X X
63.4 X
70.4 X X X X X
80.4 X X X X X X
90.4 X X X X X X X
100.4 X X X X X X X X
110.4 X X X X
120.4 X X X X X X X X
130.4 X X X X
140.4 X X X X X X
150.4 X X X X X X X X X X
160.4 X X X X
180.4 X X X X X X
200.4 X X X X X X X X X
250.4 X X X X
300.4 X X X X
350.4 X X
405 X X X X X
505 X X X X